Study and Specification of Optimal Liquid Phase Sintering Temperature for Production of Tungsten-Copper Composite

Document Type : Original Reaearch Article

Authors
Mahdi Saghafi 1
Behrouz Ghasemi 1
Iman Babaei Nejad 2
1 University of Semnan, Department of Material and Metallurgy Engineering, Semnan, Iran
2 University of Malek Ashtar, Tehran, Iran
10.30501/jamt.2636.70301
Abstract
In this research, elemental powder mixture of pure tungsten and copper powders was prepared after 1 hr of mixing, and pressed under a load of 500 MPa. Samples from the pressed mixture were liquid phase sintered in a furnace under pure hydrogen atmosphere at different temperatures (1150-1200-1300-1400 ͦC) for 2 hrs. Structure, grain size, density, hardness and strength of produced samples after sintering were studied in different temperatures. Results showed that increasing in temperature up to 1300 ͦC results in increasing in density, hardness and strength. However, at 1400 ͦC due to extensive number of voids among tungsten particles, these properties were found to decrease. The microstructure was associated with wide and deep holes.
Keywords
Tungsten
Copper
Powder metallurgy
Liquid phase sintering
Composite
  1. Abu-Oqail, A. , Ghanim, M. , El-Sheikh, M. , El-Nikhaily, A, “Effects of processing parameters of tungsten–copper composites”, Int. Journal of Refractory Metals and Hard Materials, 2012, 35, 207–212.
  2.  Roosta, Mostafa, Baharvandi, Hamidreza, Abdizade, Hossein , “An experimental investigation on the fabricationof W-Cu composite through hot-press ”, International Journal of Industrial Chemistry, 2012,112.
  3. التفات احمدی، مهدیه ملک زاده، سید خطیب الاسلام صدرنژاد، فصلنامه علمی پژوهشی مهندسی مواد مجلسی ، 1390 ، جلد ،5- 27 . 34
  4.  Maneshian, M. H., Simchi, A., Razavi Hesabi, Z. , “structural changes during synthesing of nanostructred W20%Cu composite powder by mechanical alloying”, Material science and engineering A, 2007, 86-93.
  5.  Kumar Sahoo, Prasanta , Kalyan Kamal, Sarika Srinivas, Premkumar, M. , Bojja Sreedhar, M. , Srivastava, Suneel Kumar, Durai, Loganathan “Synthesis, characterization and densification of W\Cu nanocomposite powders”, Int.
    Journal of Refractory Metals and Hard Materials, 2011, 29, 547–554.
  6.  Kang, L. , Joong, Suk, “Sintering Densification, Grain Growth, and Microstructure”, Elsevier, Burlington, 2005.
  7.  Taghavi Pourian Azar, G., Rezaie, H. R. , Razavizadeh, H. , “Synthesis and consolidation of W–Cu composite powders with silver addition”, Int. Journal of Refractory Metals and Hard Materials, 2012, 31, 157–163.
  8.  Zhigang Li, Chengchang Jia，Yuntao He， Liliang Chen, “Kinetic characteristics of liquid phase sintering of mechanically activated W-15%Cu powder”, Journal of university of science and technology Beijing, 2006,13, 4, 338- 45.
  9.  Xiaoliang, SHI. , Shuwei, Vyang. , Zhang Qiaoxin, Xingyong. , Yufu, Wang. , “Effects of Activated Sintering Process on Properties and Microstructure of W15Cu Alloy”, Journal of Wuhan University of Technology-Material Science, 2010, 25 , 909-913.
  10.  Ardestani, M. , Rezaie , H. R. , Arabi, H. , Razavizadeh, H. , “The effect of sintering temperature on densification of nanoscale dispersed W–20–40%wt Cu composite powders”, Int. Journal of Refractory Metals & Hard Materials, 2009, 27, 862-867.
  11.  Ghaderi Hamidi, A. , Arabi, H. , Rastegari, S. , “A feasibility study of W-Cu composites production by high pressure compression of tungsten powder ”, Int. Journal of Refractory Metals and Hard Materials, 2011, 29, 123– 127.
  12. Ibrahim, A. , Abdallah, M. , Mostafa, S. F. , Abousree Hegazy, A. , “An expreimental investigation on the W-Cu composites” , Materials and design, 2009, 30, 1398-1403.  
Journal of Advanced Materials and Technologies
Volume 4, Issue 2
Summer 2015
Pages 63-69

  • Receive Date 31 January 2014
  • Revise Date 31 July 2015
  • Accept Date 15 August 2015