Investigation of microstructure, mechanical and wear properties of nanocomposite Al-5%Cu/SiC produced by powder metallurgy method

Authors
L. Vafaie
A. Monshi
E. Karamian
Department of Materials Engineering, Najafabad Branch, Islamic Azad University
10.30501/jamt.2010.70231
Abstract
This study investigated and compared mechanical and wear properties and microstructure of Al-5%Cu/SiC nanocomposites with 2, 4 and 8 weight percent of SiC. Powder metallurgy method was used to successfully fabricate the nanocomposites. After milling, the resulted powder was cold pressed into pellets at a pressure of 100 MPa. Then the samples were sintered at 590 °C for 1 hour in an argon atmosphere. Densitometry, hardness, compression and bending strength and wearing of pin on the disk tests were performed for all samples. The microstructure was examined by scanning electron microscopy (SEM) and optical microscopy. Phase analysis was conducted using XRD method. The sample with 4wt% of SiC had the maximum density and minimum porosity. However, the best compressive strength and bending strength results were obtained for samples with 0 and 2wt% SiC, respectively. In the wear resistance experiments, the proportion of the slope of the weight loss due to abrasion to distance travelled by the sample was 0.039. In the nanocomposites studied there are some problems like unwetability and difference in thermal expansions between the matrix and the reinforcement; however, addition of up to 8wt% nano SiC can increase the hardness by 50%.
Keywords
Aluminum-based Nano Composite
copper
Silicon carbide
Powder Metallurgy
  1. Suryanarayana. C., "Mechanical alloying", Marcel Dekker, USA ,New York. (2004).
  2.  Fogagnolo. J.B., Amador. D., Ruis-Navas. E.M., Torralba J.M., "Solid solution in Al-4.5wt%Cuproduced by mechanical alloying", 2006, Materials Science and Engineering. 433 45-49.
  3.  Cory. A.S., "Discontinusly reinforcement for metal matrix composites", Handbook. 21, Composites, The ASM Handbook Comitte, ASM International,1th edition. (2001) 51-55.
  4.  Adamiak. M., Fogagnolo J.B., Ruiz-Navas. E.M., Dobrzanski. L.A., Torralba. J.m., "mechanically milled AA6061/(Ti3Al)p MMC reinforced with intermetallics-the structure and properties", Materials Processing. 155-156 (2004) 2002-2006.
  5.  Zhou. J., Duszczyk. J., "Liquid phase sintering of AA2014-based composite prepared from an elemental powder mixture", Journal of Materials Science. 34 (1999) 545-550.
  6.  Moon. K., Park. H.S., Lee. K.S.,"Consolidation of nanocrystalline Al-5 at.% Ti alloy powder by ultra high-pressure hot pressing", Materials Science and Engineering A. 323 (2002) 293-300.
  7.  Parvin. N., Assadifard. R., Safarzadeh. P., Sheibani. S., Marashi. P., " Preparation and mechanical properties of SiC-reinforced Al6061 composite by mechanical alloying", Materials Science and Engineering A.492 (2008) 134-140.
  8.  Available from:URL:http://www.Engineering Tool Box.com, Last visit June 2013.
  9. منشی، احمد.، سرامیکها و مواد نسوز، انتشارات جهاد دانشگاهی  دانشگاه صنعتی اصفهان، 1375.
Journal of Advanced Materials and Technologies
Volume 2, Issue 4
Winter 2013
Pages 27-34

  • Receive Date 22 July 2013
  • Revise Date 09 February 2014
  • Accept Date 12 February 2014