Assessment Of Dissimilar 6061-T6 Al/DP590 Dual Phase Steel Welds Produced Using Friction Stir Spot Welding

Authors
Amin Niroumand-Jadidi
Seyed Farshid Kashani Bozorg
University of Tehran, School of Metallurgy and Materials Engineering, Center of Excellence for Surface Engineering and Corrosion Protection of Industries, Tehran, Iran.
10.30501/jamt.2637.70318
Abstract
Dissimilar 6061Al alloy/DP590 dual phase steel joints were fabricated using friction stir spot welding. The influence of rotation speed and dwell time on the feasibility of sound joints were examined by microstructural and mechanical evaluations. Microstructural examinations by optical and scanning electron microscopy exhibited fine grains structure in the stir zone of aluminum and dominant ultrafine ferrite grains with mean grain size of less than a micron and minor martensite at ferrite grain boundaries in the steel side. In addition, an intermetallic component layer was produced along the joint interface; its thickness was a function of process parameters. The tensile-shear strength of the joint was initially found to increase with increasing of tool rotation speed at constant dwell time and then decrease with further increasing. Same trend was observed with increasing of dwell time at constant tool rotation speed. Tensile-shear strength is influenced by the thickness of the intermetallic layer. A maximum tensile-shear strength of 205MPa
was achieved for the joint produced using tool rotation and dwell time of 2000rpm and 4s, respectively; this is higher than the shear yield strength of 6061-T6 Al.
Keywords
Friction stir spot welding
Dissimilar joining
Aluminum Alloy
Dual-phase steel
Ultra-fine grains
  1. Reilly, A., "Modelling of Friction Stir Spot Welding", Ph.D. Thesis, University of Cambridge, 2013.
  2. Liyanage, T., Kilbourne, J., Gerlich, A. P., and North, T. H., "Joint Formation in Dissimilar Al Alloy/Steel and Mg Alloy/Steel Friction Stir Spot Welds", Science and Technology of Welding and Joining, 2009, 14, 500-508.
  3. Bozzi, S., Helbert-Etter, A. L., Baudin, T., Criqui, B., and Kerbiguet, J. G., "Intermetallic Compounds in Al 6016/IF-Steel Friction Stir Spot Welds", Materials Science and Engineering A, 2010, 527, 4505-4509.
  4. Bakavos, D., and Prangnell, P. B., "Effect of Reduced or Zero Pin Length and Anvil Insulation on Friction Stir Spot Welding Thin Gauge 6111 Automotive Sheet", Science and Technology of Welding and Joining, 2009, 14, 443-456.
  5. Miyagawa, K., Tsubaki, M., Yasui, T., and Fukumoto, M., "Spot Welding Between Aluminium Alloy And Low-Carbon Steel by Friction Stirring", Welding International, 2009, 23, 559-564.
  6. Mishra, R. S., and Mahoney, M. W., Friction Stir Welding and Processing, 1st ed., p. 235, ASM International, Ohio, 2007.
  7. Yang, X. W., Fu, T., and Li, W. Y., "Friction Stir Spot Welding: A Review on Joint Macro- and Microstructure, Property, and Process Modelling", Advances in Materials Science and Engineering, 2014, 2014, 11-18.
  8. Vander Voort, G. F., ASM handbook – metallography and microstructures, ASM International, California, 2004.
  9. Wang, D. A., Lee, S. C., "Microstructures and failure mechanisms of friction stir spot welds of aluminum 6061-T6 sheets", Journal of Materials Processing Technology, 2007, 186, 291-297.
  10. Sato, Y. S., Urata, M., and Kokawa, H., "Parameters Controlling Microstructure and Hardness During Friction-Stir Welding of Precipitation-Hardenable Aluminum Alloy 6063", Metallurgical and Materials Transactions A, 2002, 33, 625-635.
  11. Son, Y. I., Lee, Y. K., Park, K. T., Lee, C. S., Shin, D. H., "Ultrafine grained ferrite-martensite dual phase steels fabricated via equal channel angular pressing: Microstructure and tensile properties", Acta Materialia, 2005, 53, 3125–3134.
  12. Figner, G., Vallant, R., Weinberger, T., Schrottner, H., Pasic, H., and Enzinger, N., "Friction Stir Spot Welds Between Aluminium and Steel Automotive Sheets: Influence of Welding Parameters on Mechanical Properties and Microstructure", Welding in the World, 2009, 53, 13-23.
  13. Sun, Y. F., Fujii, H., Takaki, N., and Okitsu, Y., "Microstructure and Mechanical Properties of Dissimilar Al Alloy/Steel Joints Prepared by a Flat Spot Friction Stir Welding Technique", Materials and Design, 2013, 47, 350-357.
  14. Sarkar, R., Pal, T. K., and Shome, M., "Microstructures and Properties of Friction Stir Spot Welded DP590 Dual Phase Steel Sheets", Science and Technology of Welding and Joining, 2014, 19, 436-442.
  15. Ohashi, R., Fujimoto, M., Mironov, S., Sato, Y. S., and Kokawa, H., "Effect of Contamination on Microstructure in Friction Stir Spot Welded DP590 Steel", Science and Technology of Welding and Joining, 2009, 14, 221-227.

  • Receive Date 10 December 2015
  • Revise Date 29 May 2016
  • Accept Date 31 May 2016